pds PHG600-68-50-1-0907 1 PHG600-68-50 n fiber reinforced thermosetting preimpregnated materials for aircraft interior parts. n woven fabric of e-glass filament yarn style 7781, 296 g/m 2 , 8h satin, pr eimpr egnated with 53% phenolic r esin ph600. n self-adhesive r esin system for sandwich panel application n non-halogenated resin formulation n excellent fst behaviour n outstanding adhesion to core materials n adjustable tackiness and r etarded flow during curing n long shelf and shop life www.datasheet.co.kr datasheet pdf - http://www..net/
description PHG600-68-50 consists of a e-glass fabric style 7781, impregnated with the phenolic resin ph600. this resin is a halogen-free and self-adhesive phenolic system designed for w ide variety of manufacturing processes, retarded flow during curing, excellent heat-release and smoke-density properties and outstanding adhesion to cores and metallic substrates. the prepreg is very suitable for the manufacturing of light- weight composite sandwich structures for aircraft interior with high interlaminar shear strength and oustanding adhesion to honeycomb cores. its tackiness is adjustable between dry and t acky to meet the fabrication requirements for press cured flat parts as well as vacuum or autoclave cured complex parts. both monolithic and sandwich structures can be easily manufactured with this prepreg. the curing can be performed by press, vacuum and autoclave moulding with a pressure of at least 0.07 mpa. this prepreg meets the following airbus material performance specification: n abs5047-08 n aims 05-10-002 (certification) cured laminates fulfil the flame-retardant specifications: n f ar 25.853 (self-extinguishing) n abd 0031 the prepreg material is suitable for: n aviation and aerospace industries n marine and automotive applications 2 pds PHG600-68-50-1-0907 pr epr eg properties t est method v alue resin phenolic pr epreg weight en 2329 620 + 30 g/m 2 v olatile en 2330 (180 / 10 min) < 8.0 % resin flow en 2332 (4 plies, 140, 10 min, 4 bar) > 15 % tackiness adjustable tack fiber material e-glass fabric weight en 2331 296 g/m 2 + 5% weave style 8h satin service temperature (cured state) -55 c up to +90 resin content en2331 53.0 + 3% delivery form and storage prepreg sizes roll length / roll width 50 / 1.0 m storage life (from delivery date) days at rt / months at -5 60 / 6 www.datasheet.co.kr datasheet pdf - http://www..net/
pds PHG600-68-50-1-0907 3 curing conditions temp. () standard results flexural strength (warp) r t 80 iso 178 3 30 290 mpa flexural modulus (warp) r t 8 0 iso 178 1 6 1 4 gpa t ensile strength (warp) r t 8 0 iso 527-4 2 70 2 30 mpa tensile modulus (warp) rt iso 527-4 gpa interlaminar t e nsile shear str ength (warp) r t 80 aitm 1.0019 13 12 mpa climbing drum peel 1 rt 80 en 2243-3 130 110 n/75 mm bending load (4-p.) 1 r t 80 aitm 1.0018 970 620 n tg (tma) 140 c c ycle t emperature 1 25/135/155 c ure time 120/75/30 min s pec. pressure 0 .07 mpa heat-up 3 k/min from 60c (max) cool-down 4 k/min to 60 remove material at a t least 60 recommended curing process p ress, autoclave, vacuum-bag mechanical properties (typical values) t est methods max. mean values flammability vertical, 60s flaming burn length after flame time after flame time of drips aitm 2.0002a < 100 0 0 mm s s max. specific optical smoke density within 4 min flaming mode aitm 2.0007a < 5 ds heat release aitim 2.0006 < 35 kw m 2 heat release rate aitim 2.0006 < 65 kw - min m 2 burning behavior 2 1) sandwic h 2 plies/side; core: 3.2-48 k g/m 3 9.4 mm (hone y comb) 2) laminate 1 ply cured www.datasheet.co.kr datasheet pdf - http://www..net/
4 pds PHG600-68-50-1-0907 notice the data have been obtained from representative sample specimens. because the properties depend strongly on the fabrication and testing conditions, gurit cannot guarantee t hat the data listed above will be achieved with other processes and equipment. gurit (zullwil) ag fabrikweg 54 ch-4234 zullwil switzerland t +41 (0) 61 795 06 01 f +41 (0) 61 795 06 04 gurit (kassel) gmbh ot to-hahn-str . 5 d-34123 kassel germany t +49 (0) 561 99 85 63 0 f +49 (0) 561 99 85 63 22 e info@gurit.com w www.gurit.com www.datasheet.co.kr datasheet pdf - http://www..net/
|
